Monolithic tube sheet and method of manufacture

ABSTRACT

A monolithic refractory ceramic tube sheet for use in all-ceramic air-to-air indirect heat exchangers, the heat exchanger used in medium to high temperature, and high pressure applications. A method for forming the monolithic tube sheet includes-casting a refractory ceramic in a mold, where portions of the mold comprise the housing of the heat exchanger. Precisely formed negatives are used to form through channels and vacancies within the tube sheet, which are precisely positioned within the mold allowing uniform and flush formation of openings that receive the ceramic tubes therein. The same mold is used to provide both tube sheets of a tube sheet pair allowing accurate alignment of tubes within the exchanger vessel resulting in ease of assembly and equal loading of tubes when in use.

BACKGROUND OF THE INVENTION

Heat exchangers are devices built for efficient heat transfer from onefluid to another. Conventional heat exchangers accomplish this heattransfer using a wide variety of interfaces and fluids. This inventionis concerned with indirect heat transfer between two fluids of differenttemperatures across a dividing wall. More specifically, this inventionis concerned with an indirect air-to-air heat exchanger, for use in hightemperature, high pressure applications, which uses an array of paralleltubes extending lengthwise within an elongate hollow vessel. The arrayof tubes is supported at each end of the vessel using a tube sheet. Tubesheets are used to receive the terminal ends of the tubes such that thetubes extend in a direction normal to the tube sheet face. The terminalends of the tubes are seated within through channels in the tube sheetthat allows fluid to pass between the interior of the tube and theopposing side of the tube sheet. A housing that forms the heat exchangervessel encloses the tubes and tube sheets. In the ideal heat exchanger,there is no fluid leakage at the interface of the tube sheet and vesselwalls, and there is no fluid leakage at the interface of the tube sheetand tube. The vessel housing includes a dome at each end of the vesselthat channels fluid to or from the tube sheet. The heat exchanger vesselis also provided with transversely aligned inlet and outlet ports thatallow a second fluid to flow within the body of the vessel about theexterior of the tubes.

In such heat exchangers, a first fluid is passed from within a dome at afirst end of the heat exchanger, through the tube sheet, through theinterior of each tube within the tube array, through a second tubesheet, exiting through a second dome at the second end of the heatexchanger. A second fluid enters the body of the heat exchanger vesselthrough an inlet port such that it passes transversely through the tubearray, passing about the exterior of the tubes, and exiting the vesselvia the outlet port. The heat exchangers may be used as described as asingle unit, or may be attached in series, dome to dome, with additionalvessels to form a heat exchange system.

It is well understood that heat transfer is equally efficient regardlessof whether the heating fluid is designated to be the first fluid and theheated fluid to be-second fluid, as it is to allow the opposite to bethe case. For purposes of discussion of this invention, we will considerthe first fluid to be the fluid to be heated, and the second fluid to bethe heating fluid.

This invention is also concerned with heat exchangers operated at highpressures. For purposes of discussion, the first fluid is provided athigh pressure, that is to say, that the fluids within the domes andtubes are at high pressure. As a result, the outer (dome) side of thetube sheet is at a high pressure, and relatively low temperature, whilethe inner (vessel) side of the tube sheet is at a relatively lowpressure and high temperature.

An example of such a heat exchange system is found in a turbine powergeneration system wherein the first fluid is compressed and then heatedwithin the heat exchanger, the heated compressed fluid then being usedto propel an expander to generate power. In this system, the second,heating fluid is the exhaust gas of a manufacturing process.

Conventional heat exchangers, operating in the temperature range of 800to 1200 degrees F., and under pressures in the range of 0.25 to 2 psig,are constructed using metal tubes and tubes sheets. Typically, the metaltubes are secured to metal tube sheets by welding, or other well-knownmeans. Such heat exchangers fail when operated at higher temperatures,and have a short life span when used with corrosive fluids as found inexhaust gases from industrial operations.

Heat exchangers that must operate in more severe conditions, as found inthis invention, are fabricated with ceramic components. Such heatexchangers function well in moderate (1200 degrees F.) to high-(2800degrees F.) temperatures, at high pressures (15 psig and greater), andare resistant to corrosive fluids. Ceramic tubes and tube sheets arewell suited to use in severe operating conditions. However, the materialproperties of ceramics generate other design considerations. Forexample, loads need to be distributed evenly across the tube array toprevent any one tube from being overloaded. Thermal expansion of boththe tubes and the tube sheets needs to be considered in the design so asto avoid additional stresses at the interface between these components.Finally, fluid leakage between the first and second fluids, such asfound at the interface between tube and tube sheet, as well as betweenthe tube sheet and vessel walls must be addressed.

The prior art ceramic tube sheets, such as the tube sheet disclosed inU.S. Pat. No. 5,979,543 to Graham, have been formed of plural individualceramic tiles, each ceramic tile receiving and supporting multipleceramic tube-ends. The individual ceramic tiles are then assembled andcemented together to form a generally planar tube sheet. Disadvantagesto this type of tube sheet are fluid leakage at the cemented jointbetween tiles, and difficulty obtaining exact and precise alignment oftiles both within a tube sheet and between tube sheet pairs. Precisealignment between tube sheet pairs is required since it preventsproblems with tube assembly, and insures that the tubes are equallyloaded during operation.

SUMMARY OF THE INVENTION

The invention is a unitary (one-piece) ceramic tube sheet for use inheat exchangers, and the method of manufacturing the same. Morespecifically, the invention is a monolithic refractory ceramic tubesheet for use in all-ceramic air-to-air indirect heat exchangers, theheat exchanger used in medium to high temperature, and high pressureapplications such as extraction of thermal energy from industrial wastegases for use in a wide variety of applications such as heating cleanambient air.

By forming the ceramic tube sheet as a unitary block or monolith, thefluid leakage between joined ceramic tiles, as in the prior art iseliminated. Fabrication and assembly of the tube sheet is vastlysimplified since multiple small tiles do not have to be assembled andcemented together. Additionally, since the same form may be used tocreate both tube sheets used within a single heat exchanger, thealignment of ceramic tubes between tube sheet pairs is easilyaccomplished. This precise alignment of the tubes between the tube sheetpairs is critical since it prevents problems with tube assembly, andinsures that the tubes are equally loaded during operation.

The monolithic refractory ceramic tube sheet is described in combinationwith an adjustable, articulating, sealing plug. The plug is provided ina length such that it extends across the thickness of the tube sheet,and the exterior is provided with threads adjacent the outer (dome side)face of the tube sheet. These threads engage mating threads formed inthe tube sheet through channels, allowing the position of the plug to belongitudinally adjusted within the through channel. This ability toadjust the longitudinal position of the plug allows compensation forvariations in tube length, and ensures that each tube can be equallyloaded at assembly. Additionally, the plug can be completely removedfrom the outer face of the inventive tube sheet, allowing replacement ofa ceramic tube from the dome-side of tube sheet, or outside the heatexchanger itself Adjacent to the inner (tube side) face of the tubesheet, the plug is provided with an articulated, sealing joint whichreceives and supports the terminal ends of a ceramic tube. This jointallows rotational motions of the terminal end of the tube, and preventsfluid leakage within the through channel.

A method for forming the monolithic tube sheet is provided. Casting arefractory ceramic in a mold, where portions of the mold comprise thehousing of the heat exchanger, forms the monolithic tube sheet. Thus,the tube sheet is cast in place within the housing. This is advantageoussince the tube sheet takes on the form of the shell, minimizing fluidleakage between the casting and the shelf wall. Additionally, this stepfurther reduces steps in the assembly of the heat exchanger. Preciselyformed negatives are used to form through channels and vacancies withinthe tube sheet, which are carefully and precisely placed within themold. This precision allows uniform and flush formation of openings thatreceive the ceramic tubes therein, which is critical so that whenassembled and in use each ceramic tube can be equally loaded.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 an exploded perspective view of a partial assembly of a heatexchanger, illustrating the use of a pair of monolithic tube sheets tosupport the terminal ends of ceramic tubes.

FIG. 2 is a side section view of a monolithic tube sheet illustratingthe longitudinal orientation of the through channels as well as therelationship of the cast plate to the outer shell.

FIG. 3 is a side section detail view of a portion of the monolithic tubesheet of FIG. 2, illustrating the O-ring groove formed in the outer faceof the tube sheet and the configuration of insulation at outer shellwall.

FIG. 4 is a side section detail view of a portion of the monolithic tubesheet of FIG. 2, illustrating the tube through channel configuration.

FIG. 5 is a side section detail view of a portion of the monolithic tubesheet of FIG. 2, illustrating the widening of the tube through channelat its intersection with the outer face of the tube sheet.

FIG. 6 is a side section detail view of a portion of the monolithic tubesheet of FIG. 2, illustrating the vacancy formed at the intersection ofthe tube through channel and the inner face of the tube sheet forreceiving a ball seal therein.

FIG. 7 is a side section view of the assembled tube sheet mold.

FIG. 8 is a side section detail view of a portion of the assembled tubesheet mold of FIG. 7, illustrating the securement of the negatives tothe bottom plate of the mold using a precisely positioned through bolt.

FIG. 9 is a side section view of the tube sheet mold, illustratingplacement of insulation material along a portion of the outer shell walland along a portion of the inner flange.

FIG. 10 is a side section view of the assembled tube sheet mold withcasting material within the mold and the top plate in place.

FIG. 11 is a top perspective view of the assembled tube sheet moldillustrating the central opening in the top plate that allows thenegatives to extend beyond the top plate, and also provides a means bywhich casting material is added to the mold.

FIG. 12 is a side sectional detail view of a tube assembled within athrough channel, illustrating a second embodiment of the inventive tubesheet which employs an adjustable, articulating plug within the throughchannel.

DETAILED DESCRIPTION OF THE INVENTION

Monolithic Tube Sheet

Referring to FIGS. 1 and 2, the inventive tube sheet 10 will now bedescribed in detail. Tube sheet 10 is a monolithic refractory ceramicplate for use in all-ceramic air-to-air indirect heat exchangers. Theseceramic heat exchangers are used in medium to high temperature, and highpressure applications where metal components are unsuitable. One suchapplication is the extraction of thermal energy from industrial wastegases for use in heating clean ambient air it is, however, within thescope of this invention to employ the inventive concept in other severeenvironment applications, which include, but are not limited to, thosefound in the power and aerospace industries.

The indirect heat exchanger of this invention allows efficient heattransfer from one fluid to another across a tube wall. A first fluid ispassed through an array of parallel, elongate tubes such that it flowswithin the tube interior spaces. The tube array is enclosed within avessel. A second fluid is passed through the vessel and about theexterior of the tubes such that it flows in a direction perpendicular tothe tube array. It is important to note that the heat exchanger willfunction equally well regardless of whether the heating fluid flowswithin the tubes or about their exterior. For purposes of describing theinstant invention, the first fluid, which travels through the hollowinterior of the tubes, is clean ambient compressed air that is to beheated. The second fluid is a hot, contaminated industrial waste exhaustgas, and is used as the heating medium. The second fluid passes in across flow across and about the tubes, heating the first fluid.

Within the illustrative heat exchanger 1, a pair of opposed tube sheets10 are used at either end of the heat exchanger vessel to support theterminal ends 3, 4 of multiple elongate tubes 2 which lie in a parallelconfiguration in alignment with longitudinal axis 5 of heat exchanger 1.Tubes 2 are supported between tube sheets 10 such that they are underlongitudinal compression. This compression loading is used to improvethe function of a seal at the junction of tube 2 and tube sheet 10.

For purposes of description of this invention, the number of tubesemployed is 52, the tube outer diameter is approximately 2.5 inches, thetube inner diameter is approximately 2 inches, and the tube length isapproximately 10 feet. The array of tubes is surrounded by vessel walls6, which include inflow 7 and outflow 8 ports, aligned perpendicularlyto longitudinal axis 5, which provide for cross-flow of the second fluidacross and around the tube array. However, it is understood that thenumber of tubes employed, tube diameter, and tube length are determinedby the neat transfer requirements of the specific application, andvaries from heat exchanger to heat exchanger. Any dimensions providedherein are to illustrate scale and proportion, and may be altered tomeet the design requirements of a specific application.

Tube sheet 10 is a monolithic, or single-piece, refractory ceramic plate15 enclosed within a shell 30. Plate 15 is provided with an inner face20 that faces the interior space of the heat exchanger vessel, and anouter face 22, which is opposed to inner face 20 and separated from itby the thickness of plate 15. Inner face 20 and outer face 22 aremutually bounded by peripheral edge 24. Inner face 20 and outer face 22are parallel planes that lie perpendicular to the longitudinal axis 5 ofheat exchanger 1.

Within the illustrative heat exchanger 1 described herein, plate 15 hasa circular cross section. It is within the scope of this invention,however, to form tube sheet 10 with other cross sectional shapes whichinclude, but are not limited to, polygons, as required by the designrequirements of the specific application. Within heat exchanger 1, tubesheet 10 is subjected to high longitudinal pressures on outer face (domeside) 22, as well as opposing longitudinal pressures on inner face 20due to the compression loading of tubes 2. The combined weight of theplural ceramic rods is supported by inner face 20.

In the illustrative embodiment, plate 15 is approximately 60 inches indiameter and approximately 12½ inches thick. Thus tube sheet 10 isprovided with a diameter to thickness ratio of approximately 5 to 1.This thick plate design compensates for the opposing longitudinal loadson plate 15 due to compressed fluid pressures on outer face 22 andcompression pressures on tubes 2 on inner face 20, as well as thetransverse load on inner face 20 due to the weight of the ceramic tubes,taking into consideration material properties and safety factors. It isunderstood that plate diameter and thickness are determined by designrequirements of the specific application and will vary from heatexchanger to heat exchanger. Any dimensions provided herein are toillustrate scale and proportion, and may be altered to meet the designrequirements of a specific application. However, it should also beunderstood that in all designs for this application, the ratio ofdiameter to thickness of plate 15 is relatively large, resulting inplate 15 having a substantive thickness.

Through channels 28 extend through the thickness of plate 15 such thatthey intersect inner face 20 and outer face 22, providing fluidcommunication between the opposing sides of the tube sheet 10. Throughchannels 28 have a circular cross section and are of generally uniformdiameter across the thickness of plate 15, except at the regionsadjacent to the respective inner 20 and outer 22 faces. This diameter isapproximately that of the inner diameter of tube 2, which in theillustrative embodiment is approximately 2 inches. The number of throughchannels 28 corresponds exactly to the number of tubes 2. Each terminalend 3, 4 of each respective tube 2 is received within an arcuate sealvacancy 80 formed in through channel 28 at the inner face 20 of tubesheet 10.

To prevent fluid leakage between terminal ends 3, 4 of tube 2 and tubesheet 10, a seal is used at each respective terminal end 3, 4. Referringto FIG. 6, seal vacancy 80 is formed at the intersection of throughchannel 28 and inner face 20, and is sized and shaped to receive a sealtherein. In the preferred embodiment, seal vacancy 80 is generallyspherical in shape so as to receive the preferred seal therein. Thepreferred seal is a innovative three oint ball seal which is describedin detail in U.S. Pat. No. 6,206,603, that issued on March 27, 2001.Seal vacancy wall 82 is coated with a smooth, fine grain, hightemperature cement 84 to provide a uniform and imperfection-free surfacethat will optimize the performance of the seal.

Outer face 22 is enclosed within dome 9. When tube sheet 10 is locatedat the fluid inlet side of heat exchanger 1, outer face 22 serves todirect the first fluid into through channels 28 and thus tubes 2. Whentube sheet 10 is located at the fluid outlet side of heat exchanger 1,outer face 22 serves to direct the outflow of the first fluid fromthrough channels 28. The heat exchanger unit may be used as a singleentity, or may be attached in series (dome 9 to dome 9) with other heatexchanger units. As illustrated in FIG. 3, O-ring channel 29 is adepression formed on outer face 22 adjacent to but spaced apart fromperipheral edge 24. O-ring channel 29 is provided with a half-roundcross sectional profile. Positioning of O-ring channel 29 on outer face22 is determined by thermal considerations. In the illustrativeembodiment, O-ring channel 29 is spaced -approximately 3½ inches fromperipheral edge 24, resulting in a circular channel of approximately 53inches diameter on outer face 22. However, it is understood that channelspacing relative to peripheral edge 24 may be adjusted to accommodatethe design considerations of a specific heat exchanger.

When assembled to dome 9, an O-ring is received within O-ring channel 29as a gasket to prevent fluid and pressure leakage between tube sheet 10and dome 9. Specifically, the O-ring maintains pressure within the heatexchanger vessel by preventing fluid from bypassing tube sheet 10 andpassing through the porous, permeable insulation 60, 62 (discussedbelow) used between tube sheet 10 and shell 30. The O-ring forces fluidto pass through tube sheet through channels 28 and subsequent tubes 2.In the preferred embodiment, the O-ring is formed of round, seamlesscopper tubing of ½ inch outer diameter. In use, the O-ring is compressedbetween tube sheet 10 and dome 9, forming an effective seal. Additionalsealing may be obtained by coating outer face 22 with a caulk-like hightemperature (1500 degrees F.) sealing compound prior to assembly.

Through channel 28 is provided with a widened portion 90 at itsintersection with outer face 22. As shown in FIG. 5, this region ofthrough channel 28 adjacent to the intersection with outer face 22 isprovided with a gradually increasing diameter and the intersectionbetween the through channel 28 and the outer face forms a rounded convexshoulder. This widening and rounding of the opening prevents a pressuredrop from occurring at the outer face as the first fluid passes to orfrom tube 2 into dome 9.

Tube sheet 10 is enclosed by a thin-walled hollow cylindrical shell orhoop 30. Shell 30 provides a means to attach tube sheet 10 to the heatexchanger vessel 6, and bears longitudinal load due the high pressureswithin the heat exchanger vessel. Shell 30 is provided with a shellouter face 34, which corresponds to the exterior surface of the heatexchanger 1 in the region surrounding tube sheet 10. Shell interior face32 is opposed to shell exterior face 34 and separated from it by thethickness of the shell wall. Shell interior face 32 confronts peripheraledge 24 of tube sheet plate 15. Shell 30 is provided with a shell outeredge 36 and shell inner edge 38. Shell outer edge 36 is opposed to shellinner edge 38, and separated from it by the longitudinal length of theshell.

Outer flange 40 extends outwardly from shell exterior face 34 such thatit overlies shell exterior face 34 adjacent to shell outer edge 36, andis aligned flush with shell outer edge 36. Outer flange 40 is providedwith 56 flange through holes 49 that extend through its height, equallyspaced adjacent to and along the flange exterior face 44. Flange throughholes 49 are aligned with corresponding flange through holes on asimilar flange provided on dome 9, and receive fasteners therein tosecure the outer portion of tube sheet 10 to dome 9.

Inner flange 50 abuts shell inner edge 38 such that it forms a T-shapedcross section where shell 30 is represented by the vertical portion ofthe T, and inner flange 50 is represented by the cross portion of the T.The cross portion has an interior leg 53 which extends radially inwardtoward longitudinal axis 5, which is also referred to as the mantle.Exterior leg 51 extends radially outward away from longitudinal axis 5,relative to shell 30. Interior leg 53 of inner flange 50 takes theentire thrust of the high longitudinal pressures on outer face (domeside) 22 of tube sheet 10 within the heat exchanger vessel, and istherefore a relatively substantial member. In the illustrativeembodiment, inner flange 50 is approximately 4 inches thick, andinterior leg 53 extends inwardly from shell 30 approximately 6 inches.

Inner flange 50 is provided with a flange interior face 52 and flangeexterior face 54 that is opposed to flange interior face 52. Innerflange 50 is also provided with a flange first face 56 and a flangesecond face 58 which is opposed to flange first face 56. Along interiorleg 53, flange first face 56 confronts inner face 20 of plate 15adjacent to peripheral edge 24.

Exterior leg 51 is used to secure the inner portion of tube sheet 10 toa flange on vessel walls 6. Exterior leg 51 is provided with 56 flangethrough holes 59 which extend through its height, equally spacedadjacent to and along the flange exterior face 54. Flange through holes59 are aligned with corresponding flange through holes on the vesselwall flange, and receive fasteners therein to secure the inner portionof tube sheet 110 to a flange on vessel walls 6.

In the preferred embodiment, shell 30 is fabricated from steel. It is,however, within the scope of the invention to form shell 30 from othermaterials that are able to meet design requirements. In the preferredembodiment, outer flange 40 and inner flange 50, also fabricated fromsteel, are welded to shell 30.

Portions of the interior of shell 30 are lined with thin sheet thermalinsulation. Shell interior face insulation 60 overlies shell interiorface 32 from shell inner edge 38 to a location spaced apart from shellouter edge 36. This leaves a region adjacent to shell outer edge 36 thatis not lined with insulation material. In this region, peripheral edge24 of plate 15 confronts and abuts shell interior face 32 (see FIG. 3)so as to prevent relative motion of plate 15 within shell 30, and toprevent flu id flow between the ceramic material of plate 15 and theshell due to the porosity of the insulation material.

Flange insulation 62 is positioned on the flange first face 56 atlocations that are spaced from shell interior face 32. The unlinedportion of flange first face 56 adjacent to shell interior face 32allows plate 15 to bear the operating pressure load without crushing(thus reducing the effectiveness) of flange insulation 62.

In the preferred embodiment, the material is a microporous thermalinsulation formed of bonded silica powders with reinforcing glassfilaments such as the material commercially available under the nameMICROTHERM. The sheet thermal insulation acts to reduce heat lossthrough the shell wall, maintain a desired interior temperature, andprevent thermal fatigue of the shell material by maintaining an outershell temperature of 250 deg F. during use.

An alternative embodiment of the inventive tube sheet will now bedescribed. Second embodiment tube sheet 310 (FIG. 12) is identical totube sheet 10 in that it is a monolithic ceramic refractory plate housedwithin shell 30 as described above. However, each of the plural throughchannels 328 of second embodiment tube sheet 310 are modified toaccommodate a longitudinally adjustable sealing plug 330, one of whichresides within each through channel 328 so as to receive and support theterminal ends 3, 4 of ceramic tubes 2.

Plural through channels 328 are located in the central region of tubesheet 310, and extend from inner face 320 to outer face 322 as describedabove for tube sheet 10. However, the shape of through channels 328 hasbeen modified to accommodate plug 330. The intersection of each throughchannel 328 and outer face 322 is enlarged to form vacancy 325 having agenerally circular cross section of a diameter which is greater thanthat of the through channel 328. Vacancy 325 is provided with a taperedportion 362 adjacent to outer face 322 that allows easy insertion oftube 2 and plug 330 into through channel 328. Threads 323 are providedon the remaining surfaces of vacancy 325 for engagement with matingthreads 332 on the exterior surface 336 of plug 330. With the exceptionof vacancy 325, each through channel 328 has a circular cross sectionand is of generally uniform diameter across the thickness of tube sheet310, exiting at inner face 320.

Plug 330, a generally elongate hollow tube, is provided with a first end333, a mid portion 335, and a second end 334, where second end 334 isseparated from first end 333 by mid portion 335, and is provided with anexterior surface 336 and an interior surface 337. Plug 330 resideswithin and along the entire length of each through channel 328 such thatfirst end 333 lies generally flush with outer face 322, and second end334 lies generally flush with inner face 320. Threads 332 are providedon the exterior surface 336 of first end 333. Threads 332 are sized andshaped to matingly engage threads 323 located on the surfaces of vacancy325 so as to allow securement and longitudinal positional adjustment ofplug 330 within each through channel 328.

In the preferred embodiment, plug 330 is formed of silicon carbide.However, it is well within the scope of this invention to form plug 330from alternative materials, which include, but are not limited to,silicon nitride (Si₃N₄), a ceramic body containing a percentage of athermally conductive material such as 30% alumina oxide (Al₂O₃) and 70%silicon carbide (SiC), or metallic ceramics such as metal particlereinforced ceramic tube.

To minimize fluid leakage between plug 330 and through channel 328, pluggasket 360 is provided about the exterior surface 336 of plug 330 at theintersection of mating threads 323, 332 and tapered portion 362. Pluggasket 360 is received within a gasket channel 361 formed in throughchannel 328 such a first side borders threads 323, 332, and the opposedside abuts tapered portion 362.

Plug gasket 360 is annular, and preferably a compressible ceramic. Itfunctions to absorb the expansion of these components at hightemperatures, maintaining tight conformation between plug 330 andthrough channel 328. It also provides high temperature resistance andsealing against differential pressures through a range of variable tubelengths. However, it is within the scope of this invention to use othersealing means designed for use in this extreme environment whichinclude, but are not limited to, compressible ceramic fiber mat, ceramicpaper, or high temperature (1500 degrees F.) ceramic sealant, acaulk-like substance which maintains a seal high temperature.

Second end 334 of plug 330 is provided with an articulating sealingjoint 340 and terminates in an insertion ring 350 that receives theterminal end 3,4 of ceramic tube 2. Articulating scaling joint 340 isspaced apart from insertion ring 350 such that it lies between insertionring 350 and mid portion 335. Articulating sealing joint 340 consists ofa spherical interface 345 formed through second end 334, resulting intwo abutting components 342, 343 which are capable of relativerotational motions due to the spherical shape of their mutuallyconfronting surfaces. Spherical interface 345 provides a large area ofcontact between the two articulating components 342, 343, resulting inan efficient fluid sealing mechanism between the components 342, 343, aswell as between articulating sealing joint 340 and tube sheet 310.

A portion of exterior surface 336 is removed at the terminus ofsecond-end 334 so as to form an annular shaped, longitudinally alignedextension of interior surface 337, referred to as insertion ring 350.Insertion ring 350 has an outer diameter which is less than that ofexterior surface 336 of plug 330, such that ledge 352 is formed at thediscontinuity. The outer diameter of insertion ring 350 is slightly lessthan the interior diameter of tube 2 so that in use, insertion ring 350is received within the hollow interior of terminal end 3, 4 of tube 2,supporting terminal end 3, 4. Terminal end 3, 4 surrounds insertion ring350, and abuts ledge 352.

Through channel 238 is provided with a slight tapered widening at theintersection of through channel 328 and inner face 320 of tube sheet310. This widening prevents interference between terminal end 3, 4 oftube 2 and tube sheet 310 during any deflection of tube 2 during use.

Longitudinal adjustment of plug 330 is achieved by securing plug 330 totube sheet 310 by engaging threads 332 of plug 330 with threads 323 onthe surfaces of vacancy 325 by screwing plug 330 into through channel328. This ability to adjust the longitudinal position of plug 330 withinthrough channel allows compensation for variations in tube length,ensures that each tube is equally loaded at assembly, and maximizes thesealing characteristics of articulating joint 340. Additionally, plug330 can be completely removed from outer face 322 of tube sheet 310,allowing replacement of tube 2 from the dome-side of tube sheet 310, oroutside the heat exchanger itself.

Method of Manufacture

The method of manufacturing the inventive monolithic refractory ceramictube sheet 10, intended for use in a heat exchanger operating usingtemperatures in the range of 1200 to 2800 degrees F. and pressures of 15psig or greater, will now be described in detail.

The unitary, single piece refractory plate is fabricated by casting tubesheet 10 in place, as a monolithic structure, within outer shell wall 30of heat exchanger 1. Plate 15 of tube sheet 10 is formed of a castablerefractory ceramic material. The material selected to form plate 15 isrequired to have thermal expansion characteristics compatible with thoseof the ceramic tubes, have crushing strength characteristics which meetthe pressure requirements of the ends of the heat exchanger vessel, andto be relatively resistant to thermal shock.

Suitable refractory materials for this application include, but are notlimited to, those bonded with calcium aluminate cements, those bondedwith hydratable alumina, or those bonded with phosphates. Aggregates canrange in composition containing various quantities of bauxite, tabularalumina, fused aluminas, fused silica, silicon carbides, natural andsynthetic mullite, flint, spinels and magnesias. In the preferredembodiment, the castable refractory ceramic is formed of calciumaluminate bonded with mullite, bauxite, and calcined aluminas.

Method step 1. Provide a mold 100 to receive the cast refractorymaterial (FIG. 7). The components of mold 100 include a bottom plate110, a top plate 150, cylindrical shell 30, and negatives 160, 180 forforming vacancies within mold 100.

Shell 30, described above, provides the cylindrical outer wall of mold100. As previously discussed, the cylindrical shape of shell 30 is usedfor illustrative purposes. It is well within the scope of this inventionto provide shell 30 with other cross sectional shapes, which include,but are not limited to, polygons. Bottom plate 110 and top plate 150 aredescribed below as cylindrical in shape, but those skilled in the artwill recognize that the shape of these components can be modified toaccommodate variation in the shape of shell 30.

Bottom plate 110 comprises a short cylindrical cold rolled steel castingplate 120 that sits concentrically on a short cylindrical alignmentplate 130.

Casting plate 120 has a casting plate upper surface 122, and a castingplate lower surface 124; a height of approximately 4½ inches and adiameter of approximately 48 inches. Casting plate upper surface 122 ismachined to ensure a precisely flat, true surface.

Alignment plate 130 has an alignment plate upper surface 132, andalignment plate lower surface 134, a height of approximately 1 inch anda diameter of approximately 67 inches. Alignment plate 130 is providedwith 56 peripheral through holes 118 that extend through its heightequally spaced adjacent to and along the peripheral edge of alignmentplate 130. Peripheral through holes 118 are predrilled with the exactpattern of the holes of inner flange 50, and thus are used as areference or guide to align bottom plate 110 with shell 30, and toensure that bottom plate 110 is centered on longitudinal axis 5 of tubesheet 10. When assembled, bolts 199 extend through both peripheralthrough holes 118 and flange through holes 59 so as to secure bottomplate 110 to shell 30.

Casting plate lower surface 124 is secured to alignment plate uppersurface 132′ such that the casting plate and alignment plate areconcentric. Inner flange 50 of shell 30 is secured to the alignmentplate upper surface 132 such that the peripheral edge of casting plate120 confronts and abuts flange interior face 52 of inner flange 50. Theouter diameter of casting plate 120 is sized so as to be received withininner flange 150 with a tight fit so that casting material is not ableto seep between these confronting members.

Bottom plate 110 also provided with 52 predrilled negative-locatingthrough-holes 116 through the combined thickness of the casting plate120 and alignment plate 130, arranged within a generally geometric,preferably rectangular area. This geometric area is centered on thecenterline of bottom plate 110 and spaced apart from its peripheraledge, where the centerline is co-linear with longitudinal axis 5.Through holes 116 are precisely positioned and used to secure negatives160, 180 in the desired location on casting plate upper surface 122.

Precise positioning of negative-locating through-holes 116 is criticalsince an exact match is required for alignment of tubes 2 with anopposing tube sheet mounted at an opposite end of the heat exchangervessel. To this end, mold components bottom plate 110, top plate 150,and negatives 160, 180 are used twice, to fabricate both tube sheets foruse in a single heat exchanger. Negative-locating through holes 116 arearranged in a geometric layout that determines the arrangement of thetube array within vessel 6. As shown in FIGS. 1 and 4, tube throughchannels 28 are arranged about the centerline 5 of heat exchanger 1 in arectangular grouping, with the centers of through channels 28 onalternating rows staggered so as to maximize the uniformity of heattransfer across the array.

Referring now to FIG. 8, plural arcuate ball seal negatives 160 are usedto create vacancies in the inner face 22 of tube sheet 10. In thepreferred embodiment, each ball seal negative 160 is provided with agenerally spherical body portion 162, a truncated upper surface 164, anda truncated lower surface 166. Upper surface 164 is provided with anupwardly extending tab, up-set 168. Up-set 168 is received within alower end of through channel negative 180′ as a means to align andanchor through channel negative 180 on the upper surface 164 of ballseal negative 160.

It is understood that the shape of the ball seal negative 160 is notlimited to the generally spherical shape described above. The shape ofthe negative is determined by the shape of the seal employed at thejunction between the terminal end of tube 2 and tube sheet 10. In thisinvention, a generally spherical ball seal is the preferred sealingdevice, but other sealing mechanisms may be substituted. Thus, providingnegatives having alternative exterior shapes, which correspond toalternative sealing mechanisms, are well within the scope of thisinvention.

Each, ball seal negative 160 is located on upper surface of castingplate in alignment with a negative-locating through-hole 116 and securedby a core bolt 190 that through the bottom plate 110. Ball sealnegatives 160 must be exactly flush with upper surface of casting plate120 to prevent seepage of castable material between casting plate 120and the lower surface 166 of ball seal negative 160.

In the illustrative embodiment, 52 ball seal negatives are formed ofnylon and machined to exact tolerances. In the preferred embodiment, thematerial used to form ball seal negatives 160 is ultra high molecularweight polyethylene. This material is selected because of its ability tomaintain the desired shape under the weight of the refractory materialwhen being cast, while being flexible enough such that the refractorymaterial will not crack during the curing stage. It is well within thescope of this invention, however, to fabricate ball seal negatives 160from machined materials or materials cast from urethane, plastic, orrubber.

Plural through channel negatives 180 are used to create fluid throughchannels within the unitary, single piece refractory plate 15. Throughchannel negatives 180 are fabricated of an elongate section of plasticpipe. The pipe is provided with an enlarged upper end 182 which is sizedand shaped to provide the shaped widening 90 at the outer face 22 oftube sheet 10, and a mid portion 186 and lower end 184 of uniform outerdiameter sized to meet the requirements if the inner diameter of thetube sheet through channels 28. Hollow lower end 184 slides over up set168 so as to secure and align through channel negative 180 to the upperend 168 of ball seal negatives 160.

Core bolt 190 is long enough to extend completely through bottom plate110, ball seal negative 160, and through channel negative 180. Core bolt190 is secured to the alignment plate lower surface 134 using a firstnut 191 and washer 192, to the upper surface 164 of ball seal negative160 using a second nut 193 and washer 194, and to the upper end 182 ofthrough channel negative 180 using a third nut 195 and washer 196.

The number of through channel negatives 180 corresponds exactly to thenumber of through channels required within tube sheet 10. In theillustrative embodiment, 52 through channel negatives are provided. Inthe preferred embodiment, the polyvinyl chlorate (PVC) is used to formthrough channel negatives 180. As in the case of ball seal negatives160, the material is selected because of its ability to maintain thedesired shape under the weight of the refractory material when beingcast, while being flexible enough such that the refractory material willnot crack during the curing stage. It is well within the scope of thisinvention to fabricate through channel negatives 180 from machinedmaterials or materials cast from urethane, plastic, or rubber.

Top plate 150 comprises a cylinder having a top plate upper surface 152and a top plate lower surface 154. Top plate 150 is a short cylinder,having an approximate height of 1″ and approximate diameter of 67 inchesin the illustrative embodiment. The purpose of top plate 150 is tocreate a flush refractory casting surface that corresponds to tube sheetouter face 22. Central opening 158, a large opening in the centralportion of top plate 150, surrounds upper ends 182 of through channelnegatives 180, and provides an opening in mold 100 through whichrefractory ceramic material is cast. Central opening 158 may be providedin a generally circular shape (FIG. 11), or may be provided in anyconvenient alternative shape including, but not limited to, polygonal.

Lower surface 154 of top plate 150 is provided with an outwardlyextending half-round bead 156. Bead 156 extends about the periphery oftop plate 150 such that it is spaced apart from both its peripheral edgeand central opening 158. In use, bead 156 extends into the cast materialand forms O-ring channel 29 in tube sheet outer face 22.

Top plate 150 is provided with 56 peripheral through holes 155 whichextend through its height, equally spaced adjacent to and along theperipheral edge of top plate 150. Peripheral through holes 155 arepredrilled with the exact pattern of the holes of outer flange 40, andare used to secure top plate 150 to shell 30 during the castingprocedure. When assembled, bolts 197 extend through both peripheralthrough holes 155 and outer flange through holes 49 so as to top bottomplate 150 to shell outer edge 36.

Method step 2. Coat negatives 160, 180 with release agents.

Method step 3. Line portions of the mold with sheet insulation materialso as to reduce heat loss through the shell wall, maintain a desiredinterior temperature, and prevent thermal fatigue of the shell materialby maintaining an outer shell temperature of 250 deg F. during use.Insulation (shell insulation 60) is placed overlying shell interior face32 from shell inner edge 38 to a location spaced apart from shell outeredge 36. Insulation (flange insulation 62) is also positioned on flangefirst face 56 of inner flange 50 at locations that-are spaced from shellinterior face 32.

Method step 4. Prepare refractory ceramic material as a wet mix.

Method step 5. Cast the monolithic refractory ceramic plate 15 byplacement of mold 100 on top of a vibrating table, and pouring the wetmix into mold 100 through top plate central opening 158, between topplate 150 and plural through channel negatives 180.

Method step 6. After the refractory is cast into the mold, vibrate themold (electrically or pneumatically) to remove air pockets from thematerial and provide a dense, uniform mass. The preferred refractoryceramic material requires 2800-3000 vibrations per minute forapproximately 20 minutes.

Method step 7. The entire mold 100 with cast refractory material isleveled to ensure a finished product having inner 20 and outer 22 faceswhich are normal to the cylindrical walls of shell 30.

Method step 8. The entire leveled form with cast refractory material iscovered with a bi-layer covering which consists of an inner layer of wetburlap and an outer layer of plastic. This bi-layer covering preventsquick dehydration- and formation of a “skin”, and allows slow maturationof the casting. A curing compound may also be used to provide a uniformcure and prevent pocketing of water.

Method step 9. Allow to air dry for 24-48 hours, depending on thethickness of plate 15.

Method step 10. Remove top plate 150 from monolithic plate 15.Additional drying time may be required.

Method step 11. Remove bottom plate 110 and plural ball seal negatives160, leaving shell 30 in place about plate 15 and leaving the pluralthrough channel negatives 180 in place within plate 15.

Method step 12. Coat seal vacancy wall 82 with a smooth, fine grain,high temperature air-setting cement 84 to provide a uniform andimperfection-free surface which will optimize the performance of theseal.

Method step 13. Place casting on a rack in a curing furnace and cure attemperatures to remove free and chemical water, and to burn out throughchannel negatives. Curing is completed in a 72 hour ramp cycle.

The method steps described above provide the inventive unitary, singlepiece refractory tube sheet 10, which is cast in place, as a monolithicstructures within the cylindrical walls of shell 30 for use in heatexchanger 1.

While we have shown and described the preferred embodiment of ourinvention, it will be understood that the invention may be embodiedotherwise than as herein specifically illustrated and described, andthat certain changes in the form and arrangements of parts and thespecific manner of practicing the invention may be made within theunderlying idea or principles of the invention within the scope of theappended claims.

1. A monolithic refractory ceramic plate for supporting the terminalends of elongate ceramic tubes, said plate comprising an inner face, andan outer face opposed to said inner face and separated from the innerface by the thickness of the plate, said plate further comprising alongitudinal axis which lies normal to both said inner face and saidouter face, each of said inner face and said outer face comprising aperipheral edge, said plate comprising an outer wall which correspondsto the thickness of the plate and extends between said inner face andsaid outer face, said plate comprising a central region which issurrounded by and spaced apart from said outer wall, said central regionbeing centered on said longitudinal axis, said plate comprising aplurality of through channels sized to receive the terminal ends ofelongate tubes, said plurality of through channels being located in saidcentral region and aligned in parallel with said longitudinal axis. 2.The monolithic refractory plate of claim 1 wherein each of saidplurality of through channels comprise an inner end which intersectssaid inner face of said plate, and each of said plurality of throughchannels comprise an outer end which intersects said outer face of saidplate, wherein said inner end of each of said plurality of throughchannels is provided with a widened portion adjacent said inner face,said widened portion comprising an arcuate vacancy which is sized andshaped to receive an arcuate sealing member therein.
 3. The monolithicrefractory plate of claim 2 wherein said widened portion is providedwith a coating to provide a uniformly smooth surface.
 4. The monolithicrefractory plate of claim 2 wherein said outer end of each of saidplurality of through channels is provided with a widened portionadjacent said outer face such that the intersection between each of saidplurality of through channels and said outer face forms a rounded convexshoulder.
 5. The monolithic refractory plate of claim 4 wherein saidplate is fabricated in the shape of a cylinder, and said cylinder has athickness and a diameter, said plate being fabricated to have a diameterto thickness ratio of approximately 5 to
 1. 6. The monolithic refractoryplate of claim 1 wherein said plate further comprises a shell, saidshell comprising a hoop formed in the shape of a hollow cylinder, saidhoop having a thickness and a height, said hoop comprising a hoop innerface and a hoop outer face, the hoop inner face being opposed to andseparated from the hoop outer face by the thickness of the hoop, wherethe thickness of the hoop is small relative to the height of the hoop,said hoop comprising a first hoop edge and a second hoop edge, the firsthoop edge being opposed to the second hoop edge and separated from it bythe respective hoop inner and outer faces, and said hoop inner faceconfronts and abuts at least a portion of said outer wall of said plate.7. The monolithic refractory plate of claim 6 wherein said hoopcomprises a first flange and a second flange, wherein said first flangelies adjacent to said first hoop edge, and wherein said second flangelies adjacent to said second hoop edge.
 8. The monolithic refractoryplate of claim 7 wherein insulation means is provided between portionsof said outer wall of said plate and said hoop inner face, and whereininsulation means is provided between portions of said second flange ofsaid hoop and inner face of said plate.
 9. A unitary ceramic tube sheetfor supporting the terminal ends of plural elongate ceramic tubes withina heat exchanger operating using temperatures in the range of 1200 to2800 degrees F. and pressures of at least 15 psig, the tube sheetcomprising a single, unitary plate, the plate comprising a centralregion and a peripheral region, said central region surrounded by andconcentric with said peripheral region, the central region comprising aplurality of through holes sized and shaped to receive the terminal endsof said plural elongate ceramic tubes therein, the peripheral regioncomprising securement means for securing said tube sheet within a heatexchanger.
 10. The unitary ceramic tube sheet of claim 9 wherein theperipheral region-further comprises insulation means for maintaining aminimum required temperature in said peripheral region during use. 11.The unitary ceramic tube sheet of claim 9 wherein the plate comprises aninner face and an outer face, said inner face being opposed to saidouter face and separated from it by the thickness of said plate, theplate comprising a longitudinal axis which lies perpendicular to bothsaid inner face and said outer face, wherein said plurality of throughholes extend through the thickness of said plate such that they lie inparallel with the longitudinal axis, each of said plurality of throughholes comprising a circular cross section of a first diameter, each ofsaid plurality of through holes having an enlarged region adjacent tosaid inner face such that the intersection of each of said plurality ofthrough holes with said inner face comprises a circular cross section ofa second diameter, wherein the second diameter is greater than the firstdiameter.
 12. The unitary ceramic tubes sheet of claim 11 wherein eachof said plurality of through holes having an enlarged region adjacent tosaid outer face such that the intersection of each or said plurality ofthrough holes with said outer face comprises a tapering cross section,said tapering cross section having a minimum diameter at a locationspaced from said outer face, and a maximum diameter at said intersectionwith said outer face.
 13. The unitary ceramic tube sheet of claim 12wherein said plate is fabricated in the shape of a cylinder, and saidcylinder has a thickness and a plate diameter, said plate beingfabricated to have a plate diameter to thickness ratio of approximately5 to
 1. 14. A method of casting a unitary, single piece refractory platefor supporting the terminal ends of elongate ceramic tubes within a heatexchanger operating using temperatures in the range of 1200 to 2800degrees F. and pressures of at least 15 psig, the unitary, single piecerefractory plate being fabricated using the following method steps: Step1. Provide a mold where the mold includes a steel bottom plate, topplate, cylindrical shell, plural ball seal negatives, and plural throughchannel negatives, wherein said bottom plate comprises a shortcylindrical casting plate which sits concentrically on a shortcylindrical alignment plate of larger diameter than the casting plate,said plural ball seal negatives are used for forming vacancies toreceive spherical ball seals therein, said plural ball seal negativesbeing machined to exact tolerances, coated with release agents, andmounted to an upper surface of the casting plate, said plural throughchannel negatives are used for forming generally cylindrical throughchannels within the unitary, single piece refractory plate, said pluralthrough channel negatives being machined to exact tolerances, coatedwith release agents, and then secured to an upper end of a respectivesaid plural ball seal negative, said cylindrical shell comprises ahollow cylinder, said cylinder comprising an outer diameter, an firstedge, an second edge, said first edge being opposed to and separatedfrom said second edge by the height of the cylinder, the cylindercomprising an inner surface and an outer surface, said inner surfacebeing opposed to and separated from the outer surface by the thicknessof the cylinder, the cylinder comprising a first flange which extendsfrom said first edge of said cylinder and a second flange which extendsfrom said second edge of said cylinder, said top plate comprises a shortcylinder having a top plate diameter, a top plate upper surface, and atop plate lower surface, wherein said top plate diameter is equal to theshell outer wall diameter, such that in use, the alignment plate issecured to the first flange of the cylindrical shell such that thecasting plate is concentric with and surrounded by the first flange,such that the periphery of the alignment plate abuts a lower face of thefirst flange, such that an upper face of the casting plate and an upperface of the first flange provide a bottom surface for the mold, and suchthat the cylindrical shell provides outer walls for the mold, the pluralball seal negatives are secured to the bottom surface of the mold usingprecisely located predrilled through holes within the bottom plate, thetop plate is secured to the second flange of the cylindrical shell, thetop plate comprising a centrally aligned opening which surrounds theplural through channel negatives such that the plural through channelnegatives extend upward through said centrally aligned opening therein,Step
 2. Line portions of the mold with sheet insulation material so asto maintain an outer shell temperature of 250 deg F. during use, Step 3.Cast the unitary, single piece refractory plate by placement of saidmold on top of a vibrating table, preparation of refractory material asa wet mix, and pouring said wet mix into said mold through the top platecentrally aligned opening, said top plate centrally aligned openingbeing sized to provide a space between the top plate and each of saidplural through channel negatives, Step
 4. After the refractory is castinto the mold, it is vibrated to remove air pockets from the materialand provide a dense, uniform mass, Step
 5. The entire mold with castrefractory is leveled to ensure a finished product having surfaces thatare square relative to cylindrical shell walls, Step
 6. The entireleveled mold with cast refractory is covered with an inner layer of wetburlap and an outer layer of plastic so as to prevent quick dehydration,to prevent formation of a skin, and to allow slow maturation of thecasting, Step
 7. Allow to air dry for at least 24 hours, Step
 8. Removetop plate from said unitary, single piece refractory plate casting, Step9. Remove bottom plate and plural ball seal negatives, leaving thecylindrical shell about said unitary, single piece refractory platecasting and leaving the plural through channel negatives in place withinthe said unitary, single piece refractory plate casting, Step 10.Prepare and treat any cosmetic surface blemishes due to air bubbles inmold during maturation found in plural ball seal vacancies using asourizing cement, Step
 11. Place casting on a rack in curing furnace toremove free and chemical water, and to burn out through channelnegatives, and cure for approximately 72 hours.
 15. The method ofcasting a unitary, single piece refractory plate of claim 14 whereinsaid portions of said mold which are lined with said sheet insulationmaterial comprise the inner surface of the cylindrical shell atlocations spaced from said second edge of said cylindrical shell, and aportion of said first flange which both confronts said refractory plateand which is spaced apart from said inner surface of said cylindricalshell.
 16. The method of casting a unitary single piece refractory plateof claim 14 wherein said top plate lower surface is provided with anoutwardly extending bead, said bead comprising a half-round crosssection, said bead spaced from the peripheral edge of said top platesuch that it forms a circular channel in the top face of the casting forreceiving gasketing material therein.
 17. A method for forming aunitary, single-piece refractory tube sheet for supporting the terminalends of elongate ceramic tubes within a heat exchanger operating usingtemperatures in the range of 1200 to 2800 degrees F. and pressures of atleast 15 psig, the unitary, single piece refractory tube sheet beingfabricated by casting in place, as a monolithic structure, within anouter shell wall of the heat exchanger.
 18. The method for forming saidunitary, single-piece refractory tube sheet of claim 17 wherein a moldis used to form said casting of said unitary, single piece refractorytube sheet, wherein said mold comprises a cold-rolled steel bottomplate, a top plate, said cylindrical outer shell wall, plural machinedball seal negatives for forming ball seal sockets within said unitarysingle-piece refractory tube sheet, and plural negatives for formingthrough channels within said unitary, single-piece refractory tubesheet, wherein the bottom plate comprises a short cylindrical castingplate and a short cylindrical alignment plate, said casting platecomprising a first height and first diameter, a casting plate uppersurface, and a casting plate lower surface, said alignment platecomprising a second height and second diameter, an alignment plate uppersurface, and an alignment plate lower surface, wherein said seconddiameter is greater than the first diameter and wherein said castingplate lower surface is secured to said alignment plate upper surfacesuch that the casting plate and alignment plate are concentric, each ofsaid plural machined ball seal negatives comprises an arcuate bodyportion, said body portion having a truncated upper surface and atruncated lower surface, each respective lower surface of said pluralball seal negatives being mounted to said casting plate upper surface,each of said plural negatives for forming through channels comprises anelongate body portion having an first end and a second end, wherein eachrespective second end of said plural negatives for forming throughchannels is secured to a respective upper surface of one of said ballseal negatives, said outer shell wall comprises a thin-walled hollowsteel cylinder, the cylinder comprising an upper edge, a lower edge, anda shell wall outer diameter, wherein the lower edge of the outer shellwall is secured to said alignment plate, said top plate comprising shortcylinder having a third height and third diameter, a top plate uppersurface, a top plate lower surface, and a central opening, wherein saidthird diameter is equal to the shell outer wall diameter, such that inuse, the casting plate is secured to the alignment plate, the alignmentplate is secured to the lower edge of the outer shell wall, thus formingsaid mold wherein the casting plate provides a mold bottom surface,wherein said outer shell wall provides cylindrical mold side walls, andsaid plural machined ball seal negatives and said plural negatives forforming through channels are positioned within the mold using preciselylocated predrilled through-holes within the bottom plate, and whereinthe top plate is secured to said upper edge of said outer shell wallsuch that the tube negatives extend upward through said central openingtherein, thereby forming a mold top surface, and the top plate issecured to said upper edge of said outer shell wall.
 19. The method forforming said unitary, single-piece refractory tube sheet of claim 18wherein the following method steps are used: Step
 1. Cast the tube sheetby placement of wet casting material in mold, the casting materialplaced within the mold by passing it through a vacancy between the tubenegatives and the top plate, Step
 2. Vibrate casting to remove airpockets and to density casting material, Step
 3. Level the mold toensure a finished product having surfaces that are square relative toshell walls, Step
 4. Cover the entire leveled form with a bilayercovering, said bilayer covering comprising an inner layer of wet burlapand an outer layer of plastic, said bilayer covering used to preventquick dehydration and formation of a skin, and to allow slow maturationof the casting, Step
 5. Air dry for at least 24 hours, Step
 6. Stripcasting of top plate, bottom plate, and ball seal negatives, Step 7.Place casting on a rack in curing furnace to remove free and chemicalwater, and to burn out through channel negatives, cure for approximately72 hours.
 20. The method as claimed in claim 19 wherein insulation meansare provided between portions of the outer shell wall and the castingmaterial.
 21. The method of forming said single piece refractory tubesheet of claim 19 wherein said plural machined ball seal negatives andsaid plural negatives for forming through channels are preciselypositioned on the upper surface of the casting plate using preciselylocated predrilled through holes within the bottom plate.
 22. The methodfor forming said single piece refractory tube sheet of claim 21 whereinthe top plate comprises a peripheral edge, and the peripheral edge ofsaid top plate is secured to said upper edge of said outer shell wallthereby forming a mold top surface.
 23. The method for forming saidsingle piece refractory tube sheet of claim 22 wherein the top plate isprovided with a centrally positioned opening, and the body portion ofeach of said plural negatives for forming a through channel extendsupwards through said centrally positioned opening in said top plate. 24.The method of forming said single piece refractory tube sheet of claim23 wherein said top plate lower surface is provided with an outwardlyextending bead, said bead comprising a half-round cross section, saidbead spaced from the peripheral edge of said top plate such that itforms a circular channel in the top face of the casting for receivinggasketing material therein.
 25. The method of forming said single piecerefractory tube sheet of claim 19 wherein said casting materialcomprises a calcium aluminate cement bonded with mullite, bauxite, andcalcined aluminas.
 26. The method of forming said single piecerefractory tube sheet of claim 19 wherein said plural machined ball sealnegatives are formed of ultra high molecular weight polyethylene. 27.The method of forming said single piece refractory tube sheet of claim19 wherein said plural negatives for forming through channels are formedof polyvinyl chloride.
 28. A unitary refractory ceramic tube sheet incombination with a ceramic air-to-air indirect heat exchanger, the heatexchanger for use in operation conditions which include temperatures inthe range of 1200 to 2800 degrees F. and pressures of at least 15 psig,wherein the heat exchanger comprises an array of elongate ceramic tubesin a parallel configuration housed within an elongate vessel, the vesselcomprising a vessel first end and a vessel second end, each elongateceramic tube within said array of elongate ceramic tubes comprising afirst terminal end, a second terminal end, and a body portion whichextends between said first terminal end and said second terminal end,said tube sheet comprises a single-piece, monolithic refractory ceramicplates, said plate comprising an inner face, and an outer face opposedto said inner face and separated from th e inner face by the thicknessof the plate, said plate further comprising a longitudinal axis whichlies normal to both said inner face and said outer face, saidlongitudinal axis lying parallel to each elongate ceramic tube, each ofsaid inner face and said outer face comprising a peripheral edge, eachof said inner face and said outer face comprising a central region whichis surrounded by and spaced apart from said peripheral edge, saidcentral region being centered on said longitudinal axis, said platecomprising a plurality of through channels sized to receive the terminalends of said ceramic elongate tubes, said plurality of through channelsbeing located in said central region and aligned in parallel with saidlongitudinal axis, each of said plurality of through channels comprisean inner end which intersects said inner face of said plate, and each ofsaid plurality of through channels comprise an outer end whichintersects said outer face of said plate, said tube sheet supporting therespective first terminal ends of said elongate ceramic tubes byreceiving said first terminal ends within said respective inner ends ofsaid through channels.
 29. The unitary refractory ceramic tube sheet incombination with a ceramic air-to-air indirect heat exchanger of claim28 wherein said plate is fabricated in the shape of a cylinder, and saidcylinder has a thickness and a diameter, said plate being fabricated tohave a diameter to thickness ratio of approximately 5 to
 1. 30. Theunitary refractory ceramic-tube sheet in combination with a ceramicair-to-air indirect heat exchanger of claim 28 wherein said platecomprises an outer wall which corresponds to the thickness of the plateand extends between said inner face and said outer face, said platefurther comprises a shell, said shell comprising a hoop formed in theshape of a hollow cylinder, said hoop having a thickness and a height,said hoop comprising a hoop inner face and a hoop outer face, the hoopinner face being opposed to and separated from the hoop outer face bythe thickness of the hoop, where the thickness of the hoop is smallrelative to the height of the hoop, said hoop comprising a first hoopedge and a second hoop edge, the first hoop edge being opposed to thesecond hoop edge and separated from it by the respective hoop inner andouter faces, and said hoop inner face confronts and abuts at least aportion of said outer wall of −0.20 said plate, said hoop comprises afirst flange and a second flange, wherein said first flange liesadjacent to said first hoop edge, and wherein said second flange liesadjacent to said second hoop edge.
 31. The unitary refractory ceramictube sheet in combination with a ceramic air-to-air indirect heatexchanger of claim 30 wherein insulation means is provided betweenportions of said outer wall of said plate and said hoop inner face, andis provided between portions of said second flange of said hoop andinner face of said plate.
 32. The unitary refractory ceramic tube sheetin combination with a ceramic air-to-air indirect heat exchanger ofclaim 30 wherein each of said inner ends of said plurality of throughchannels comprises an enlarged region which is sized and shaped so as toreceive a sealing member therein, and each of said outer ends of saidplurality of through channels comprises a tapering cross section, saidtapering cross section having a minimum diameter at a location spacedfrom said outer face, and a maximum diameter at said intersection withsaid outer face.
 33. A unitary ceramic tube sheet for supporting theterminal ends of plural elongate ceramic tubes within a heat exchangeroperating using temperatures in the range of 1200 to 2800 degrees F. andpressures of up to 15 psig, the tube sheet comprising a single, unitaryplate, the plate comprising a central region and a peripheral region,said central region surrounded by and concentric with said peripheralregion, the plate comprises an inner face and an outer face, said innerface being opposed to said outer face and separated from it by thethickness of said plate, the plate comprising a longitudinal axis whichlies perpendicular to both said inner face and said outer face thecentral region comprising a plurality of through holes sized and shapedto receive the terminal ends of said plural elongate ceramic tubestherein, wherein said plurality of through holes extend through thethickness of said plate such that they lie in parallel with thelongitudinal axis, each of said plurality of through holes comprising acircular cross section of a first diameter, each of said plurality ofthrough holes comprising an enlarged region adjacent to said outer facesuch that the intersection of each of said plurality of through holeswith said outer face comprises a generally circular cross section of asecond diameter, wherein the second diameter is greater than the firstdiameter, said enlarged region comprising tube sheet threads formed onthe surface thereof, the tube sheet further comprising an elongatehollow plug positioned within each of said plurality of through holes,said plug comprising a first end and a second end, said second endseparated from said first end by a mid portion, said plug comprising anexterior and an interior, wherein said exterior of said first end isprovided with plug threads formed on the surface thereof, said plugthreads sized and shaped to matingly engage said tube sheet threads soas to allow securement and positional adjustment of said plug withineach of said plurality of through holes, said second end of said plugcomprising an articulating socket, said articulating socket receivedwithin each of said plurality of through holes such that it liesadjacent to said inner face of said plate, said articulating socketreceiving and supporting the terminal end of an elongate ceramic tubetherein such that the terminal end of an elongate ceramic tube iscapable of rotational motions, said articulating socket comprising aspherical mating surface which lies between the mid portion and thesecond end, the second end terminating in a longitudinally alignedextension of the interior surface such that it extends beyond theexterior surface to form an insertion ring, said insertion ringcomprising an insertion ring exterior surface which is sized to bereceived within the interior of said elongate ceramic tube when in use.34. A combination unitary tube sheet and plural adjustable tubesecurement means, wherein said plural adjustable tube securement meansare for use in securing and adjusting the terminal ends of pluralelongate ceramic tubes supported by said unitary tube sheet within aheat exchanger vessel, wherein said unitary tube sheet comprises amonolithic refractory ceramic plate, the plate comprising an inner faceand an outer face, said inner face being opposed to said outer face andseparated from it by the thickness of said plate, a longitudinal axiswhich lies perpendicular to both said inner face and said outer face, aplurality of through holes sized and shaped to receive the terminal endsof said plural elongate ceramic tubes therein, said plurality of throughholes extending through the thickness of said plate such that they liein parallel with the longitudinal axis, and wherein one of said pluraladjustable tube securement means resides within each of said pluralityof through holes.
 35. The combination unitary tube sheet and pluraladjustable tube securement means of claim 34 wherein said pluraladjustable tube securement means comprises a plug, said plug comprisingan elongate hollow tube provided with exterior threads at a first endand a second end which is opposed to the first end, said first end ofsaid plug is received within a vacancy formed at the intersection ofeach of said plurality of through holes and the outer face of said tubesheet, said vacancy comprising a generally cylindrical void in saidouter face, said void comprising a threaded region, said threaded regionbeing sized and shaped to matingly received the exterior threads of saidfirst end of said plug therewithin.
 36. The combination unitary tubesheet and plural adjustable securement means of claim 35 wherein saidfirst end of said plug is provided a gasket between said plug and saidtube sheet for preventing fluid leakage between the plug and saidrespective through hole.
 37. The combination unitary tube sheet andplural adjustable securement means of claim 36 wherein said second endof said plug terminates in an articulating socket, said articulatingsocket receiving and supporting the terminal end of an elongate ceramictube therein such that rotational motions of the terminal end of anelongate ceramic tube are allowable.
 38. The combination unitary tubesheet and plural adjustable securement means of claim 37 wherein saidarticulating socket comprises a spherical mating surface which liesbetween the first end and the second end such that it is adjacent tosaid second end, the second end terminating in an insertion ring, saidinsertion ring comprising a longitudinal extension of the interiorsurface of the plug, said insertion ring comprising an insertion ringexterior surface which is sized to be received within the interior ofsaid elongate ceramic tube when in use.